A

Application:  For road marking paint, for shotblasting, for filler, etc

Al2O3(Composition %):   (max.3.2%)               0.4

B

B2O3                                                               0.0

C

Crush Strength(psi):    >30,000

CaO   8.0-10.0%              9.8

 

CAS # 65997-17-3 (Glass Beads)

CAS # 7631-86-9((SiO2)

CAS # 1313-59-3 (Na2O)

CAS # 1305-78-8 (CaO)

CAS # 1309-48-4 (MgO)

CAS # 1344-28-1 (Al2O3)

Components(Main, weight in %):

SiO2     71.0-73.0%

Na2O    13.0-14.5%

CaO      8.0-10.0%

MgO     Max.4.2%

Fe2O3           0.2%

Al2O3          Max.3.2%

Coefficient of Friction:                                     0.9-1.0

Composition: Soda-Lime Glass

 

D

Dielectric Constant, 22ºC，106Hz                    6.9

Diameter(Microns) and Mesh(#)

38um=400#

45um=325#

53um=270#

63um=230#

75um=200#

90um=170#

106um=140#

125um=120#

150um=100#

180um=80#

212um=70#

250um=60#

300um=50#

425um=40#

355um=45#

500um=35#

600um=30#

710um=26#

850um=20#

1000um=18#

1180um=16#

1400um=14#

1700um=12#

2000um=10#

2360um=8#

2800um=7#

3350um=6#

4000um=5#

 

E

EINECS # 266-046-0

Expansion Coefficient, in/in/ºCX10-7                     90

 

F

Fe2O3 /FeO                                                        0.2%

 

G

Grade: Drop-on / Intermix (Premix)

H

Hardness (Moh):   5-6                                          5.5

 

 

I

Iron Content:  max. 0.1% (Free)

K

K2O                                                                    0.1%

L

Loss Tangent,  22ºC，106Hz                               0.0085

Leachate PH                                                           9.4

Leach Conductivity,(mmho/cm)                               101.0

Leach Concentrations,(mg/cc)

Loading Capacity: 20-22pallets/20feet container, 20-28Tons/20feet container

M

Materials: recycled glass, virgin glass (direct melt glass), special glass

MgO   Max.4.2%:             3.3

 

 

N

Na2O(Composition %) :    13-14.5                         13.7

O

Oil Absorption*(g oil/100g. spheres)ASTM D-1483 :    18

P

Packing

PH:   9-10

Packing: net 25kgs in Plastic woven bag / Paper bag, 50bags/plywood pallet

net 500kgs/1000kgs/2000kgs/jumbo bag(big bag) with plywood pallet

 

R

Refractive Index:

Class A  n ≥ 1.5

Class B  n ≥ 1.7

Class C  n ≥ 1.9

Class D  n ≥ 2.2

Rigidity  Modulus, 106PSI                                        4.3

Retroreflectivity:

≥300mcd/m2/lx (1.5RI Glass Beads)

≥400mcd/m2/lx (1.6RI Glass Beads)

≥600mcd/m2/lx (1.6RI Glass Beads)

≥800mcd/m2/lx (1.7RI Glass Beads)

≥1000mcd/m2/lx (1.9RI Glass Beads and 2.2RI Glass Beads)

Roundness:  65%,70% ,80%, 85%, 90% ,95% according to different Standards

S

Specific Gravity(g/cm3):    2.4-4.3,                          2.5 for 1.5RI,  3.5 for 1.7RI , 4.2 for 1.9RI

Softening Point, °C:       700-800                            704

SiO2(Composition %)    :   71-73                            72.5

Size:  10-1700um

Surface treatment:

Uncoated (without any coatings)

Silicone Coated (Waterproof)

Silane Coated (Adhesion)

Dual Coated (Silicone and Silane)

T

Thermal Conductivity(cal/(sec)(cm2)(ºC/cm)at 500ºC               0.0036

Total Alkali                                                                25.7

Calcium                                                   18.1

Boron                                                       Trace

Silica                                                        5.4

V

Vol. Resistivity, 25ºC, ohm-cm                            6.5x1012

 

 

Y

Young's Modulus, 106PSI                                   10.0